ASTM B863 标准钛及钛合金丝：EV Group China 参考手册
ASTM B863 标准的技术规格与分类
ASTM B863 标准对纯钛及其多种合金丝材的生产和化学成分提出了严格要求。EV Group China 供应的产品完全符合这些标准，确保了在恶劣环境下机械性能的高度稳定性和耐腐蚀性。
| 等级 (Grade) | UNS | 合金类型 / 描述 |
|---|---|---|
| Grade 1 | UNS R50250 | 非合金钛 |
| Grade 2 | UNS R50400 | 非合金钛 |
| Grade 2H | UNS R50400 | 非合金钛 (Grade 2，最小 UTS 为 58 KSI / 400 MPa) |
| Grade 3 | UNS R50550 | 非合金钛 |
| Grade 4 | UNS R50700 | 非合金钛 |
| Grade 5 | UNS R56400 | 钛 6%Al, 4%V |
| Grade 6 | UNS R54520 | 钛 5%Al, 2.5%Sn |
| Grade 7 | UNS R52400 | 非合金钛 + Pd (0.12–0.25%) |
| Grade 7H | UNS R52400 | 非合金钛 + Pd (Grade 7，最小 UTS 为 58 KSI / 400 MPa) |
| Grade 9 | UNS R56320 | 钛 3.0%Al, 2.5%V |
| Grade 11 | UNS R52250 | 非合金钛 + Pd (0.12–0.25%) |
| Grade 12 | UNS R53400 | 钛 0.3%Mo, 0.8%Ni |
| Grade 13 | UNS R53413 | 钛 0.5%Ni, 0.05%Ru |
| Grade 14 | UNS R53414 | 钛 0.5%Ni, 0.05%Ru |
| Grade 15 | UNS R53415 | 钛 0.5%Ni, 0.05%Ru |
| Grade 16 | UNS R52402 | 非合金钛 + Pd (0.04–0.08%) |
| Grade 16H | UNS R52402 | 非合金钛 + Pd (Grade 16，最小 UTS 为 58 KSI / 400 MPa) |
| Grade 17 | UNS R52252 | 非合金钛 + Pd (0.04–0.08%) |
| Grade 18 | UNS R56322 | 钛 3%Al, 2.5%V + Pd (0.04–0.08%) |
| Grade 19 | UNS R58640 | 钛 3%Al, 8%V, 6%Cr, 4%Zr, 4%Mo |
| Grade 20 | UNS R58645 | 钛 3%Al, 8%V, 6%Cr, 4%Zr, 4%Mo + Pd (0.04–0.08%) |
| Grade 21 | UNS R58210 | 钛 15%Mo, 3%Al, 2.7%Nb, 0.25%Si |
| Grade 23 | UNS R56407 | 钛 6%Al, 4%V (ELI — 超低间隙元素) |
| Grade 24 | UNS R56405 | 钛 6%Al, 4%V + Pd (0.04–0.08%) |
| Grade 25 | UNS R56403 | 钛 6%Al, 4%V + Ni (0.3–0.8%), Pd (0.04–0.08%) |
| Grade 26 | UNS R52404 | 非合金钛 + Ru (0.08–0.14%) |
| Grade 26H | UNS R52404 | 非合金钛 + 0.08–0.14% Ru (Grade 26，最小 UTS 为 58 KSI / 400 MPa) |
| Grade 27 | UNS R52254 | 非合金钛 + Ru (0.08–0.14%) |
| Grade 28 | UNS R56323 | 钛 3%Al, 2.5%V + Ru (0.08–0.14%) |
| Grade 29 | UNS R56404 | 钛 6%Al, 4%V (ELI) + Ru (0.08–0.14%) |
| Grade 30 | UNS R53530 | 钛 0.3%Co, 0.05%Pd |
| Grade 31 | UNS R53532 | 钛 0.3%Co, 0.05%Pd |
| Grade 32 | UNS R55111 | 钛 5%Al, 1%Sn, 1%Zr, 1%V, 0.8%Mo |
| Grade 33 | UNS R53442 | 钛 0.4%Ni, 0.015%Pd, 0.025%Ru, 0.15%Cr |
| Grade 34 | UNS R53445 | 钛 0.4%Ni, 0.015%Pd, 0.025%Ru, 0.15%Cr |
| Grade 35 | UNS R56340 | 钛 4.5%Al, 2%Mo, 1.6%V, 0.5%Fe, 0.3%Si |
| Grade 36 | UNS R58450 | 钛 45%Nb |
| Grade 37 | UNS R52815 | 钛 1.5%Al |
| Grade 38 | UNS R54250 | 钛 4%Al, 2.5%V, 1.5%Fe |
| Grade 39 | UNS R53390 | 钛 0.25%Fe, 0.4%Si |
在工程实践中，EV Group China 建议优先使用 SI 单位制进行设计。带“H”后缀的版本（2H、7H、16H、26H）专为高压环境设计，在此类环境下，保证屈服强度至关重要。
行业标准与合规性
本规范由 ASTM B10 委员会维护。在能源机械和压力容器制造中使用丝材时，必须符合 ASME 规定，特别是 SB863 规范的第二部分。